"La substitution de Si \u00E0 Co dans les compos\u00E9s interm\u00E9talliques RCo5 induit des modifications importantes sur leurs propri\u00E9t\u00E9s structurales et magn\u00E9tiques. La limite de solubilit\u00E9 de Si dans RCo5 est d\u00E9pendante de la temp\u00E9rature. Tous les compos\u00E9s RCo5-xSix \u00E9tudi\u00E9s ont une structure de type CaCu5 \u00E0 haute temp\u00E9rature. Ils n\u2019ont pas besoins des paires Co-Co pour stabiliser leur structure. Les atomes de Si sont localis\u00E9s exclusivement sur le site cristallographique 3g dans tous les compos\u00E9s \u00E9tudi\u00E9s, quel que soit le taux de substitution ou la nature de la terre rare. Ce site a la particularit\u00E9 d\u2019avoir un nombre maximal d\u2019atomes R voisins. Le param\u00E8tre de maille c diminue avec l\u2019augmentation du taux de substitution Si/Co. Dans quelques compos\u00E9s avec terre rare lourds un changement de sym\u00E9trie est observ\u00E9 : la sym\u00E9trie diminu\u00E9 de hexagonale \u00E0 orthorhombique avec la r\u00E9duction de la temp\u00E9rature. Ce changement de sym\u00E9trie est induit par un l\u00E9ger d\u00E9placement, selon la direction cristallographique [210]hexa, des atomes Co2c vers des positions plus proches des atomes R. Ce d\u00E9placement est reli\u00E9 \u00E0 l\u2019alignement particulier des moments magn\u00E9tiques dans le plan (a, b). La substitution Si/Co a une influence importante sur le magn\u00E9tisme itin\u00E9rant de Co et sur le magn\u00E9tisme localis\u00E9 de R. La temp\u00E9rature d\u2019ordre et le moment magn\u00E9tique de cobalt diminuent rapidement avec la substitution. Ces modifications sont induites par la r\u00E9duction du champ d\u2019\u00E9change et l\u2019hybridation 3d(Co)-3p(Si). En combinant diff\u00E9rents types de mesures magn\u00E9tiques avec la diffraction des neutrons, des diagrammes de phases magn\u00E9tiques des RCo5-xSix ont \u00E9t\u00E9 \u00E9labor\u00E9s." . "Text" . . . . . "The Si for Co substitution in the RCo5 intermetallic compounds induces important modifications of the magnetic and crystal properties of this series of compounds. The solubility limit of Si in RCo5 is temperature dependent. All the compounds have a CaCu5 type structure, but no Co-Co dumbbells are needed for the stabilization of this structure. The Si atoms are localized exclusively at the 3g crystallographic sites in all the compounds, regardless of the substitution percentage or of the R atom nature. This site has the particularity of having the maximum R atoms in the first vicinity. The c lattice parameter decreases upon Si/Co substitution. In some of the heavy rare earth compounds (TbCo5-xSix, HoCo5-xSix) crystal symmetry change was observed. The symmetry lowers from hexagonal to orthorhombic with the reduction of the temperature. The symmetry change is due to the small displacement, along [210]hexa crystallographic direction, of the Co2c atoms to positions closer to the R atoms. This phenomenon is related to the particular alignment of the magnetic moments in the (a, b) plane.The Si/Co substitution has an important influence both on the itinerant magnetism of Co and on the localized one of R. The Tc and \u00B5Co decrease fast upon Si substitution. These modifications are due to the reduction of the exchange field and to the 3d(Co)-3p(Si) hybridization. Combining different magnetisation measurement with neutron diffraction the magnetic phase diagrams were elaborated for the RCo5-xSix systems." . . "Magn\u00E9tisme de Co" . "Propri\u00E9t\u00E9s structurales et magn\u00E9tiques de compos\u00E9s interm\u00E9talliques \u00E0 base des terres rares, cobalt et silicium" . . "Compos\u00E9s interm\u00E9talliques" . "Propri\u00E9t\u00E9s structurales et magn\u00E9tiques de compos\u00E9s interm\u00E9talliques \u00E0 base des terres rares, cobalt et silicium" . "Distorsion structurale" . "Structural and magnetic properties of rare earth, cobalt and silicon based intermetallic compounds" . "Th\u00E8ses et \u00E9crits acad\u00E9miques" . . "2008" . . . .