"Calcination des s\u00E9diments de drapage contamin\u00E9s, \u00E9tudes des propri\u00E9t\u00E9s physico-chimiques" . . . . . . . "The work presented deals with the NOVOSOL \u00AE process developed by SOL V A Y S.A. Company. This aim to decompose the organics and stabilize heavy metal containing contaminated dredged sediment for beneficiai reuse. This process comprises two stages: chemical treatment (addition of soluble phosphate) and the thermal treatment (calcination). Research presented is focused on the thermal treatment. Our objective is to understand the physicochemical behaviour of the sediment during the calcination. The understanding of the evolution on these properties will help for the beneficial reuse of the treated sediment in various industry such as the civil engineering. The characterization performed was followed by the investigation of the behaviour of heavy metals and the organic compounds during the calcination. The distribution of heavy metals between the solid phase and the gas phase were studied during the calcination and the result obtained showed majority of heavy metals are trapped in the solid. The leaching tests performed showed that heavy metals present in the residue are well stabilized. The degradation of the organic compounds is effective at 400\u00B0C. Afterwards, the structural change of the sediment during thermal treatment was investigated at laboratory scale and at pilot scale. An increase in specifie surface is observed until 400\u00B0C followed by a signification reduction accompanied by a densification and growing of the particles. The increase in specifie surface observed is the formation of pores observed by due to the decomposition of organics from 400\u00B0C to l000\u00B0C. The combined evolutions of properties are due to the thermal sintering of the sediments induced by the formation of grain boundary driven by the mass transport at high temperature. The calcination in a rotary kiln showed that the physical properties (the specifie surface, density, particle size) of the sediment depend on the calcination. parameters such as the residence time, calcination temperature, sediment flow rate were investigated." . "Les travaux pr\u00E9sent\u00E9s s\u2019inscrivent dans le cadre du proc\u00E9d\u00E9 NOVOSOL\u00AE d\u00E9velopp\u00E9 par la soci\u00E9t\u00E9 SOLVAY S.A. qui vise le traitement et la valorisation des s\u00E9diments de dragages contamin\u00E9s en m\u00E9taux lourds et en mati\u00E8res organiques. Ce proc\u00E9d\u00E9 de traitement comporte deux \u00E9tapes de traitements : chimique (phosphatation) et thermique (calcination). Les travaux pr\u00E9sent\u00E9s dans cette th\u00E8se ont port\u00E9 sur le traitement thermique. Notre objectif est de comprendre le comportement physico-chimique du s\u00E9diment pendant la calcination. La connaissance des ces propri\u00E9t\u00E9s permettra d\u2019utiliser le s\u00E9diment calcin\u00E9 dans diff\u00E9rentes fili\u00E8res de valorisation, notamment le g\u00E9nie civil. Deux s\u00E9diments d\u2019origines et de propri\u00E9t\u00E9s diff\u00E9rents ont \u00E9t\u00E9 \u00E9tudi\u00E9es. Apr\u00E8s la caract\u00E9risation physico-chimique, l\u2019\u00E9tude du comportement des m\u00E9taux lourds et des compos\u00E9s organiques pendant la calcination a \u00E9t\u00E9 examin\u00E9. La distribution des m\u00E9taux lourds entre la phase solide et la phase gazeuse a \u00E9t\u00E9 \u00E9tudi\u00E9e et les r\u00E9sultats obtenus ont permis de montrer que l\u2019essentiel des m\u00E9taux lourds est pi\u00E9g\u00E9 dans le solide. Les tests de disponibilit\u00E9 des m\u00E9taux ont montr\u00E9 que les m\u00E9taux lourds pr\u00E9sents dans le solide trait\u00E9 sont bien stabilis\u00E9s. Les r\u00E9sultats montrent aussi que la calcination renforce la stabilit\u00E9 des m\u00E9taux lourds. La d\u00E9gradation des compos\u00E9s organiques est effective \u00E0 partir de 400\u00B0C. Dans la seconde partie, le comportement textural et structural du s\u00E9diment sous l\u2019effet de la temp\u00E9rature a \u00E9t\u00E9 \u00E9tudi\u00E9 \u00E0 l\u2019\u00E9chelle de laboratoire et \u00E0 l\u2019\u00E9chelle pilote. Une augmentation de la surface sp\u00E9cifique est observ\u00E9e jusqu\u2019\u00E0 400\u00B0C suivie d\u2019une importante r\u00E9duction qui s\u2019accompagne d\u2019une densification et d\u2019un grossissement des particules. L\u2019augmentation de la surface sp\u00E9cifique observ\u00E9e jusqu\u2019\u00E0 400\u00B0C s\u2019explique par la d\u00E9composition des mati\u00E8res organiques qui entra\u00EEne une augmentation de la porosit\u00E9 et donc de la surface sp\u00E9cifique ; au del\u00E0 de 400\u00B0C, les \u00E9volutions conjugu\u00E9es des propri\u00E9t\u00E9s sont dues au frittage thermique des s\u00E9diments induit par la formation de joint de grains par transport de mati\u00E8re \u00E0 haute temp\u00E9rature. Les calcinations r\u00E9alis\u00E9es en four tournant pilote ont permis de montrer que les propri\u00E9t\u00E9s physiques (surface sp\u00E9cifique, densit\u00E9, granulom\u00E9trie) du s\u00E9diment d\u00E9pendent des param\u00E8tres de calcination (temps de s\u00E9jours, temp\u00E9rature de calcination, d\u00E9bit de chargement, angle d\u2019inclinaison du four). D\u2019une mani\u00E8re g\u00E9n\u00E9rale, les r\u00E9sultats montrent qu\u2019une augmentation de la surface sp\u00E9cifique est li\u00E9e \u00E0 la fois \u00E0 la r\u00E9duction de la temp\u00E9rature de calcination et \u00E0 l\u2019allongement du temps de s\u00E9jour. On note aussi un bon accord entre les r\u00E9sultats obtenus \u00E0 l\u2019\u00E9chelle laboratoire par rapport \u00E0 ce qui a \u00E9t\u00E9 obtenu \u00E0 l\u2019\u00E9chelle pilote. La taille des particules augmente quand la temp\u00E9rature de calcination est \u00E9lev\u00E9e \u00E0 cause du frittage thermique. Ces r\u00E9sultats montrent qu\u2019il est possible d\u2019obtenir des produits en fin de proc\u00E9d\u00E9 ayant des propri\u00E9t\u00E9s tr\u00E8s diff\u00E9rentes. Cela donne des perspectives int\u00E9ressantes en terme de valorisation." . "M\u00E9taux lourds" . . "Frittage (m\u00E9tallurgie)" . "Compos\u00E9s organiques" . "Dragage" . "Calcination of contaminated dredged sediments, study of chemicals and physicals properties" . . . "Th\u00E8ses et \u00E9crits acad\u00E9miques" . . . "Text" . "S\u00E9diments fluviaux" . "2008" . . . "Calcination des s\u00E9diments de drapage contamin\u00E9s, \u00E9tudes des propri\u00E9t\u00E9s physico-chimiques" . .